Xtel®XE4050BL
Polyphenylene Sulfide Alloys
Xtel® XE4050BL is a glass fiber and mineral filled PPS based alloy developed to provide high ductility and impact strength along with good thermal stability.
NOMINAL ENGINEERING PROPERTIES(1) Value Test Method
  Tensile Strength, Ksi 19.0 ASTM D638
  Elongation, % 1.7 ASTM D638
  Flexural Strength, Ksi 29.0 ASTM D790
  Flexural Modulus, Msi 1.8 ASTM D790
  Notched Izod Impact, ft·lb/in, 1/8 in specimen 1.3 ASTM D256
  Unnotched Izod Impact, ft·lb/in, 1/8 in specimen 10.0 ASTM D256
  Compressive Strength, Ksi 28.0 ASTM D695
  Heat Deflection Temperature, 264 psi,°F 490 ASTM D648
  Coefficient of Linear Thermal Exp., X 10-6 in/in/°C   ASTM E831
      Axial Direction, -50°C to 50°C 20  
      Axial Direction, 100°C to 200°C 10  
      Transverse Direction, -50°C to 50°C 50  
      Transverse Direction, 100°C to 200°C 100  
  Flammability Rating V-0(3) UL 94
  Thermal Conductivity, BTU·in/hr·ft2·°F 2.6  
  Dielectric Strength, V/mil 500 ASTM D149
  Dielectric Constant, 78° F   ASTM D150
      1kHz 4.1  
      1MHz 4.0  
  Dissipation Factor, 78°F    ASTM D150
      1 kHz 0.003   
      1 MHz 0.009   
  Volume Resistivity, ohm·cm 1 x 1015 ASTM D257
  Arc Resistance, sec 120 ASTM D495
  Comparative Tracking Index, V 150(3) UL 746A
  Mold Shrinkage(2) in/in, Flow/Transverse 0.002 / 0.004  
  Density, g/cc 1.70 ASTM D792
  Water Absorption, % 0.03 ASTM D570
  Color Black  
(1) Test specimen molding conditions:  Stock Temperature, 600-650°F; Mold Temperature, 275°F
(2) Measured on 4 in X 4 in X 1/8 in Plaques, Edge Gated
(3) This product is not currently UL Listed; test results indicate this level of performance
The nominal properties reported herein are typical of the product but do not reflect normal testing variances and therefore should not be used for specification purposes.
Xtel®XE4050BL
Polyphenylene Sulfide Alloys
Xtel® XE4050BL is a glass fiber and mineral filled PPS based alloy developed to provide high ductility and impact strength along with good thermal stability.
NOMINAL ENGINEERING PROPERTIES(5) Value Test Method
  Tensile Strength, MPa 130 ISO 527
  Elongation, % 1.7 ISO 527
  Flexural Strength, MPa 190 ISO 178
  Flexural Modulus, GPa 11 ISO 178
  Notched Izod Impact, kJ/m2 7.0 ISO 180A
  Unnotched Izod Impact, kJ/m2 35 ISO 180U
  Compressive Strength, MPa 195 ISO 604
  Heat Deflection Temperature, 1.8 MPa,°C 255 ISO 75
  Coefficient of Linear Thermal Exp., X 10-6 in/in/°C   ISO 11359-2
      Axial Direction, -50°C to 50°C 20   
      Axial Direction, 100°C to 200°C 10   
      Transverse Direction, -50°C to 50°C 50   
      Transverse Direction, 100°C to 200°C 100    
  Flammability Rating V-0(7) UL 94
  Thermal Conductivity, W/m·K 0.37  
  Dielectric Strength, kV/mm 20 ASTM D149
  Dielectric Constant, 25°C    ASTM D150
      1kHz 4.1   
      1MHz 4.0   
  Dissipation Factor, 25°C    ASTM D150
      1 kHz 0.003   
      1 MHz 0.009   
  Volume Resistivity, ohm·cm 1 x 1015 ASTM D257
  Arc Resistance, sec 120 ASTM D495
  Comparative Tracking Index, V 150(7) UL 746A
  Mold Shrinkage(6) m/m, Flow/Transverse 0.002 / 0.004  
  Density, g/cc 1.70 ISO 1183A
  Water Absorption, % 0.03 ASTM D570
  Color Black  
(5) Test specimen molding conditions:  Stock Temperature, 315-345°C; Mold Temperature, 135°C
(6) Measured on 102 mm X 102 mm X 3.2 mm Plaques, Edge Gated
(7) This product is not currently UL Listed; test results indicate this level of performance
The nominal properties reported herein are typical of the product but do not reflect normal testing variances and therefore should not be used for specification purposes.
MSDS #712830 Revision Date January, 2008
Before using this product, the user is advised and cautioned to make its own determination and assessment of the safety and suitability of the product for the specific use in question and is further advised against relying on the information contained herein as it may relate to any specific use or application. It is the ultimate responsibility of the user to ensure that the product is suited and the information is applicable to the user's  specific application. Chevron Phillips Chemical Company LP does not make, and expressly disclaims, all warranties, including warranties of merchantability or fitness for a particular purpose, regardless of whether oral or written, express or implied, or allegedly arising from any usage of any trade or from any course of dealing in connection with the use of the information contained herein or the product itself. The user expressly assumes all risk and liability, whether based in contract, tort or otherwise, in connection with the use of the information contained herein or the product itself. Further, information contained herein is given without reference to any intellectual property issues, as well as federal, state or local laws which may be encountered in the use thereof. Such questions should be investigated by the user.