PREMIUM EXTRUSION AND RIGID PACKAGING RESINS

Marlex^Ž K605
Polyethylene Resin

NOMINAL PHYSICAL PROPERTIES ⁽¹⁾	English	SI	Method
Melt Index, HLMI, 190/21.6	11.0g/10 min.	11.0 g/10 min	ASTM D1238
Tensile Strength at Yield, 2 in/min, Type IV Bar	4400 psi	30 MPa	ASTM D638
Ultimate Elongation, 2 in (50 mm)per min	>500%	>500%	D638 Type IV
ESCR, Condition A (100% lgepal), F₅₀	>50 h	>50 h	ASTM D1693
ESCR, Condition B (100% lgepal), F₅₀	>20 h	>20 h	ASTM D1693
Flexural Modulus	230,000 Psi	1586 Mpa	D790

(1) Physical properties reported herein were determined on compression molded specimens prepared in accordance with Procedure C of ASTM D1928

The nominal properties reported herein are typical of the product but do not reflect normal testing variance and therefore should not be used for specification purposes.

MSDS #E100		Revision Date July, 1995

Before using this product, the user is advised and cautioned to make its own determination and assessment of the safety and suitability of the product for the specific use in question and is further advised against relying on the information contained herein as it may relate to any specific use or application. It is the ultimate responsibility of the user to ensure that the product is suited and the information is applicable to the user's specific application. Chevron Phillips Chemical Company LP does not make, and expressly disclaims, all warranties, including warranties of merchantability or fitness for a particular purpose, regardless of whether oral or written, express or implied, or allegedly arising from any usage of any trade or from any course of dealing in connection with the use of the information contained herein or the product itself. The user expressly assumes all risk and liability, whether based in contract, tort or otherwise, in connection with the use of the information contained herein or the product itself. Further, information contained herein is given without reference to any intellectual property issues, as well as federal, state or local laws which may be encountered in the use thereof. Such questions should be investigated by the user.