PREMIUM EXTRUSION AND RIGID PACKAGING RESINS
Marlex® K605
HIGH DENSITY POLYETHYLENE

This extra high molecular weight ethylene homopolymer is tailored for large applications that:
  • Require good ESCR
  • Require exceptional rigidity
  • Require excellent melt strength
  • Are durable and recyclable for sustainability
    • Typical blow molded applications for K605 include items such as:
  • Automotive bumper beams
  • Carrier resin for mineral-reinforced HDPE masterbatches
    Typical thermoformed applications for K605 include items such as:
  • Nursery containers
  • Dunnage trays
  • Large tote boxes
    • This resin meets these specifications:
  • ASTM D4976 - PE 235
  • FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H

    • NOMINAL PHYSICAL PROPERTIES (1) English SI Method
      Density --- 0.961 g/cm3 ASTM D1505
      Flow Rate (HLMI, 190/21.6) --- 11.0 g/10 min ASTM D1238
      Tensile Strength at Yield, 2 in/min, Type IV bar 4,300 psi 30.0 MPa ASTM D638
      Elongation at Break, 2 in/min, Type IV bar 800% 800% ASTM D638
      Flexural Modulus, Tangent - 16:1 span:depth, 0.5 in/min 220,000 psi 1,510 MPa ASTM D790
      ESCR, Condition B (100% Igepal), F50 30 h 30 h ASTM D1693
      Durometer Hardness, Type D (Shore D) 64 64 ASTM D2240
      Vicat Softening Temperature, Loading 1, Rate A 263°F 128°C ASTM D1525
      Heat Deflection Temperature, 66 psi, Method A 191°F 88°C ASTM D648
      Brittleness Temperature, Type A, Type I specimen <-103°F <-75°C ASTM D746
      Tensile Impact, Type S bar 115 ft•lb/in2 240 kJ/m2 ASTM D1822
    1. The nominal properties reported herein are typical of the product, but do not reflect normal testing variance and therefore should not be used for specification purposes.  Values are rounded.  The physical properties were determined on compression molded specimens that were prepared in accordance with Procedure C of ASTM D4703, Annex A1.
    MSDS #240370 Revision Date May, 2007
    Before using this product, the user is advised and cautioned to make its own determination and assessment of the safety and suitability of the product for the specific use in question and is further advised against relying on the information contained herein as it may relate to any specific use or application. It is the ultimate responsibility of the user to ensure that the product is suited and the information is applicable to the user's specific application. Chevron Phillips Chemical Company LP does not make, and expressly disclaims, all warranties, including warranties of merchantability or fitness for a particular purpose, regardless of whether oral or written, express or implied, or allegedly arising from any usage of any trade or from any course of dealing in connection with the use of the information contained herein or the product itself. The user expressly assumes all risk and liability, whether based in contract, tort or otherwise, in connection with the use of the information contained herein or the product itself. Further, information contained herein is given without reference to any intellectual property issues, as well as federal, state or local laws which may be encountered in the use thereof. Such questions should be investigated by the user.