Marlex® HMN TR-942 / HMN TR-942G
HIGH DENSITY POLYETHYLENE

These hexene copolymers are tailored for rotational molding applications that require:
  • Wide process windows and fair flow
  • Long-term UV stabilization
  • Excellent impact strength
  • Good ESCR
    • These resins are available in:
  • Pellet form – HMN TR-942 
  • 35 US mesh powder – HMN TR-942G
    These resins meet these specifications:
  • ASTM D4976 - PE 233
  • FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per 21 CFR 176.170(c) Table 2.  Single use articles contacting food types I, II, IV-B, VI-A, VI-B, VII-B, and VIII.  Repeated use articles contacting all food types defined in 21 CFR 176.170(c) Table 1.
  • NSF / ANSI Standard 61 for potable water (CLD 23)
    • Typical applications for HMN TR-942 and HMN TR-942G include items such as:
  • Potable water and chemical tanks
  • Agricultural equipment

    • NOMINAL PHYSICAL PROPERTIES(1) (2) English SI Method
      Density --- 0.943 g/cm3 ASTM D1505
      Melt Index, 190/2.16 --- 2.0 g/10 min ASTM D1238
      ESCR, Condition A (100% Igepal), F50 700 h 700 h ASTM D1693
      ESCR, Condition A (10% Igepal), F50 250 h 250 h ASTM D1693
      Durometer Hardness, Type D (Shore D) 61 61 ASTM D2240
      Vicat Softening Temperature, Loading 1, Rate A 249°F 120°C ASTM D1525
      Brittleness Temperature, Type A, Type I specimen -103°F -75°C ASTM D746
      Melting Temperature 266°F 130°C ASTM D3418
      Crystallization Temperature 236°F 113°C ASTM D3418
    ROTATIONAL MOLDED PROPERTIES (1) (3) English SI Method
      Impact Strength, 1/8" (3.2 mm) thickness, -40 C° 68 ft·lb 92 J ARM Impact
      Impact Strength, 1/4" (6.35 mm) thickness, -40 C° 180 ft·lb 244 J ARM Impact
      Tensile Strength at Yield, 2 in/min, Type IV bar 3,000 psi 21 MPa ASTM D638
      Elongation at Break, 2 in/min, Type IV bar 720% 720% ASTM D638
      Flexural Modulus, Tangent - 16:1 span:depth, 0.5 in/min 125,000 psi 860 MPa ASTM D790
      Flexural Modulus, 2% Secant - 16:1 span:depth, 0.5 in/min 105,000 psi 720 MPa ASTM D790
      Heat Deflection Temperature, 66 psi, Method A 147°F 64°C ASTM D648
      Heat Deflection Temperature, 264 psi, Method A 111°F 44°C ASTM D648
    1. The nominal properties reported herein are typical of the product, but do not reflect normal testing variance and therefore should not be used for specification purposes.  Values are rounded. 
    2. The physical properties were determined on compression-molded specimens that were prepared in accordance with Procedure C of ASTM D4703, Annex A1.
    3. Properties were measured on rotational molded samples with 1/8” (3.17 mm) average thickness, unless otherwise noted.  The average peak internal air temperature during molding was 400ºF.
    MSDS #240370 Revision Date May, 2006
    Before using this product, the user is advised and cautioned to make its own determination and assessment of the safety and suitability of the product for the specific use in question and is further advised against relying on the information contained herein as it may relate to any specific use or application. It is the ultimate responsibility of the user to ensure that the product is suited and the information is applicable to the user's specific application. Chevron Phillips Chemical Company LP does not make, and expressly disclaims, all warranties, including warranties of merchantability or fitness for a particular purpose, regardless of whether oral or written, express or implied, or allegedly arising from any usage of any trade or from any course of dealing in connection with the use of the information contained herein or the product itself. The user expressly assumes all risk and liability, whether based in contract, tort or otherwise, in connection with the use of the information contained herein or the product itself. Further, information contained herein is given without reference to any intellectual property issues, as well as federal, state or local laws which may be encountered in the use thereof. Such questions should be investigated by the user.