TDS - CPD-700
For more information and technical
assistance contact:
Phillips Sumika Polypropylene Company
P.O. Box 4910
The Woodlands, TX 77387-4910
800.231.1212 ext 4849
Marlex® CPD-700
Engineered Thermoplastic Polyolefin, High Stiffness, High Melt Flow, Talc Filled

Nominal Physical Properties
Property English SI Method
  Density 1 g/cc 1 g/cc ASTM D1505
  Melt Flow Rate, @ 230°C 80 g/10min 80 g/10min ASTM D1238
  Tensile Strength at Yield, 50 mm/min 3900 psi 26.9 MPa ASTM D638
  Flexural Modulus, Tangent, 13 mm/min 330000 psi 2280 MPa ASTM D790
  Notched Izod Impact Strength, @ 23°C 1 ft*lbf/in 53 J/m ASTM D256
  Notched Izod Impact Strength, @ -30°C 0.4 ft*lbf/in 21 J/m ASTM D256
  Heat Deflection Temperature, @ 0.455 MPa 270 °F 132 °C ASTM D648
  Heat Deflection Temperature, @ 1.82 MPa 162 °F 72 °C ASTM D648
  Rockwell Hardness, R Scale 87 87 ASTM D785



Physical property testing performed on injection-molded specimens
The nominal properties reported herein are typical of the product but do not reflect normal testing variance and therefore should not be used for specification purposes.


MSDS #CPC00282 Revision Date June, 2004
Before using this product, the user is advised and cautioned to make its own determination and assessment of the safety and suitability of the product for the specific use in question and is further advised against relying on the information contained herein as it may relate to any specific use or application. It is the ultimate responsibility of the user to ensure that the product is suited and the information is applicable to the user's specific application. Phillips Sumika Polypropylene Company does not make, and expressly disclaims, all warranties, including warranties of merchantability or fitness for a particular purpose, regardless of whether oral or written, express or implied, or allegedly arising from any usage of any trade or from any course of dealing in connection with the use of the information contained herein or the product itself. The user expressly assumes all risk and liability, whether based in contract, tort or otherwise, in connection with the use of the information contained herein or the product itself. Further, information contained herein is given without reference to any intellectual property issues, as well as federal, state or local laws which may be encountered in the use thereof. Such questions should be investigated by the user.