Marlex® CUH-020-BLK
Talc-filled Polypropylene Impact Copolymer, Heat Stabilized, Black

Applications:
  • Blow Molded, under-the-hood parts
     


    ISO Nominal Properties
    Property SI Method
      Density 1.04 g/cc ISO 1183
      Melt Flow Rate, @ 230°C 1.0 g/10min ISO 1133
      Tensile Strength at Yield, 50 mm/min 26 MPa ISO 527
      Flexural Modulus, 2.0 mm/min 2,000 MPa ISO 178
      Notched Izod Impact Strength, @ 23°C 56 kJ/m2 ISO 180
      Notched Izod Impact Strength, @ -40°C 4.2 kJ/m2 ISO 180
      Heat Deflection Temperature, @ 0.455 MPa 99 °C ISO 75
      Heat Deflection Temperature, @ 1.82 MPa 60 °C ISO 75

    The nominal properties reported herein are typical of the product but do not reflect normal testing variance and therefore should not be used for specification purposes.


    MSDS #647390 Revision Date October, 2007
    Before using this product, the user is advised and cautioned to make its own determination and assessment of the safety and suitability of the product for the specific use in question and is further advised against relying on the information contained herein as it may relate to any specific use or application. It is the ultimate responsibility of the user to ensure that the product is suited and the information is applicable to the user's specific application. Phillips Sumika Polypropylene Company does not make, and expressly disclaims, all warranties, including warranties of merchantability or fitness for a particular purpose, regardless of whether oral or written, express or implied, or allegedly arising from any usage of any trade or from any course of dealing in connection with the use of the information contained herein or the product itself. The user expressly assumes all risk and liability, whether based in contract, tort or otherwise, in connection with the use of the information contained herein or the product itself. Further, information contained herein is given without reference to any intellectual property issues, as well as federal, state or local laws which may be encountered in the use thereof. Such questions should be investigated by the user.