ForSField™ SG11 Protective Coating

ForSField™ SG-11 protective coating is a surface tolerant, zero VOC, HAPs free, direct to metal (DTM), multipurpose, two part protective coating designed for spray applications. It has excellent adhesion to metal, concrete, and galvanized substrates. Its main purpose is to protect substrates from corrosion and impart superior chemical resistance. Can be used as a primer, tie coat, top coat, and for chemical immersion service. It is available in gray.

Features

  • Free of VOCs,  HAPs, and solvents
  • Convenient 1:1 volumetric mix ratio
  • Self priming and surface tolerant
  • Bio-content is 26% by weight
  • Exceptional resistance to acids, bases, and chemicals
  • Excellent adhesion to steel, galvanized steel, and concrete substrates
  • Resists corrosion

Dry Film Thickness and Coverage

  • 11-15 mils (+/- 2 mils) DFT  recommended for atmospheric  service
  • 15-25 mils (+/- 5 mils) DFT  recommended  for immersion service
  • 50 mils DFT Maximum
  • Up to 20 mils maximum per pass (to prevent sagging)
  • Theoretical coverage of 123 ft2/gal @ 13 mils
  • Theoretical coverage of 80 ft2/gal @ 20 mils

Intended Uses

For use as a medium to high-build epoxy coating to enhance corrosion and  chemical resistance in a range of environments including petrochemical plants,  mining facilities, pulp and paper mills, chemical process plants, and offshore  structures. It can be used as a primer or a top coat. Recommended film builds  are 11-15 mils for most applications and 15-25 mils for immersion applications. It  can be used over tightly adhering rust to encapsulate it and prevent further  corrosion. This coating is suitable for both maintenance and new construction  applications.

Surface Preparation

ForSField™ SG-11 protective coating is a surface tolerant coating so it is able  to maximize adhesion to substrates that are not perfectly prepared and  encapsulates existing rust. This is very useful for maintenance applications were perfect surface preparation might be very difficult to achieve. Since this coating  shows excellent adhesion to tightly adhering rust it can be used under these  non-ideal conditions. A lower degree of surface preparation will affect adhesion to the surface. The surface to be coated should be clean and dry. Utilize  sufficient methods to eliminate excess debris, scale, rust, water, or oil that may  interfere with coating adhesion. It is recommended to wipe clean all metal surfaces with a solvent such as methyl ethyl ketone (MEK) after surface  preparation and before coating application. For best results the following surface preparation is recommended.
 
Concrete
Concrete surfaces should be fully cured, cleaned and degreased. For optimal  adhesion performance acid etching is recommended by using muriatic acid or a similar product.
 


 
Steel
For optimal results prepare the surface in accordance with SSPC-SP 5 / NACE 1/ Sa. 3 / BS4232 First Quality / 31 GP 404 Type 1 / JASh3 or JASd3, white metal  blast cleaning for atmospheric and immersion service. An anchor profile of 3-4 mils is recommended.
 


 
As an alternative prepare the surface in accordance with SSPC-SP 6 / NACE 3 /  Sa. 2 / BS4232 Third Quality / 31 GP 404 Type 2 / JASh 1 or JASd 1,  commercial blast cleaning for atmospheric service. A minimum anchor profile of 1.5 mils is recommended.
 
Can be applied over galvanized steel after surface preparation in accordance to  SSPC-SP 1 solvent cleaning with MEK.
 
Previously Painted Surfaces
ForSField™ SG-11 protective coating can be applied over most coatings in  sound condition but compatibility needs to be tested beforehand. We  recommend to sand or abrade to roughen and de-gloss the surface. Then solvent wipe the surface with MEK. Ensure the surface is dry and free from  excess dust or debris before applying this coating.
 

Performance Data

All of the data presented are reported from tests performed on coatings applied  under controlled laboratory conditions and may not represent exact values  achieved in field applications.
 

 

Application

Listed below are general guidelines for the application of the ForSField™ SG-11.  Specific project conditions may require modifications to these guidelines to  achieve the desired results. Ensure the ambient temperature, unmixed product  components and surface to be coated are above 55°F (13°C). Both components  should be no warmer than 130°F (54°C) at the time of spray application. Best  results are achieved with a relative humidity of 60% or less and a surface  temperature of at least 5°F (3°C) above the dew point.
 
Mixing and Spray Application
  • Mix ratio is 1:1 by volume
  • Thinning is not recommended
  • Plural component airless spray equipment capable of heating coating to  130ºF and provide in line pressures of 4,500 psi at the tip
  • Re-use of SG-11H hardener is not recommended and opened containers  should be discarded at the end of the day
  • Recommended clean-up solvent is MEK
 
HEAT WARNING! Curing epoxy generates significant heat. Never hand mix the  ForSField™ SG-11R epoxy resin with the ForSField™ SG-11H hardener. Doing so will generate excessive heat and the combined materials may, if not used promptly, reach temperatures which can cause burns to skin (potentially as much as 300°F or higher). Do not  mix the epoxy resin with the hardener in containers made of materials such as  plastic, foam or glass. If a container of mixed epoxy resin and hardener starts to  exotherm (heat up) take precautions to move the container to a safe location.
 
For industrial/commercial use. Application must be performed by trained  personnel only using an appropriate plural component sprayer.
 

*Curing times will vary with temperature, humidity, and other application conditions.  
 

Top-Coating

  • Can be top-coated but compatibility would need to be tested beforehand
  • Allow 7 hours after applying final coat, before top-coating with other coatings
  • If the coating is older than five days, wipe surface down with MEK before  top-coating

 

Shelf Life Information

We recommend storage at a controlled temperature of 25ºC. Shelf life of the ForSField™ SG-11R Resin is 2 years in original unopened  container. Shelf life of the ForSField™ SG-11H Hardener is 2 years in original unopened  container.
 

Packaging

The ForSField™ SG-11 Protective Coating is available in pail (4 gallons), and  drum (50 gallons) quantities.
 

Product Density

Density for the ForSField™ SG-11R Resin is 12.10 lbs/gal.  Density for the ForSField™ SG-11H Hardener is 8.20 lbs/gal.
 
Technical Data Sheet
ForSField SG-11 TDS View Download
Safety Data Sheets
Area Language
United States English View Download
Synonyms: Acid Resistant coating, marine coating, pilings, splash zone, anticorrosion, industrial coating, chemical resistant coating